Abstract
Precise magnetic structures of RMn2O5, with R=Y,Ho,Bi in the commensurate and/or ferroelectric regime, have been determined by single-crystal neutron diffraction. For each system, the integrated intensities of a large number of independent magnetic Bragg reflections have been measured, allowing unconstrained least-squares refinement of the structures. The analysis confirms the previously reported magnetic configuration in the ab plane, in particular, the existence of zigzag antiferromagnetic chains. For the Y and Ho compounds, additional weak magnetic components parallel to the c axis were detected, which are modulated in phase quadrature with the a-b components. This component is extremely small in the BiMn2O5 sample, therefore supporting symmetric exchange as the principal mechanism inducing ferroelectricity. For HoMn2O5, a magnetic ordering of the Ho moments was observed, which is consistent with a superexchange interaction through the oxygens. For all three compounds, the point symmetry in the magnetically ordered state is m2m, allowing the polar b axis found experimentally.