Abstract
Metal fluoride nanocomposites are uniquely suited as an alternative pathway to provide very high energy density cathodes for lithium batteries. Contrasted with modern intercalation compounds, they undergo conversion upon discharge into nanodomains of lithium fluoride and highly active metal. The nanosized metal formed during the discharge process along with the dynamic nature of the crystal structure may have considerable impact on the stability of any solid state interphase formed through reaction with the electrolyte. This is in contrast to the more macrocrystalline and stable crystal structure of traditional intercalation compounds. It has been found that the cyclic carbonates are susceptible to decomposition on the nanometal surfaces at potentials as high as 2.00 V
vs.
Li, and the products have been identified with Field Emission Scanning Electron Microscopy (FESEM), Attenuated Total Reflectance-Fourier Transform Infrared Spectroscopy (ATR-FTIR), and X-ray Photoelectron Spectroscopy (XPS) as lithium carbonate species. Of greater importance is the impact of these decomposition products on the reversible cycling of the metal fluoride. Through a series of potentiodynamic and galvanostatic cycling trials, a clear relationship has been developed for the bismuth fluoride nanocomposites, the decomposition of the electrolyte solvent, and the cycle life. Acyclic organic carbonate solvents have been found to have minimal interaction and exhibited better long-term cycling performance than cyclic solvents.
The performance of bismuth-based nanocomposites for rechargeable Li battery cathodes was greatly influenced by the choice of organic carbonate solvent. Cyclic carbonates were found to decompose on discharge, negatively impacting cycling.